USA flag logo/image

An Official Website of the United States Government

Company Information:

Company Name:
Hjc Enterprise, Llc
Address:
5 Badgley Dr
New Providence, NJ 07974-2501
Phone:
(908) 313-8514
URL:
N/A
EIN:
208480885
DUNS:
828297353
Number of Employees:
8
Woman-Owned?:
No
Minority-Owned?:
No
HUBZone-Owned?:
No

Commercialization:

Has been acquired/merged with?:
N/A
Has had Spin-off?:
N/A
Has Had IPO?:
N/A
Year of IPO:
N/A
Has Patents?:
N/A
Number of Patents:
N/A
Total Sales to Date $:
$ 0.00
Total Investment to Date $
$ 0.00
POC Title:
N/A
POC Name:
N/A
POC Phone:
N/A
POC Email:
N/A
Narrative:
N/A

Award Totals:

Program/Phase Award Amount ($) Number of Awards
SBIR Phase I $453,899.00 4

Award List:

Alloy Composition Optimization for High Critical Density of (Nb,Ta,Ti)3Sn Superconductor

Award Year / Program / Phase:
2009 / SBIR / Phase I
Award Amount:
$98,484.00
Agency:
DOE
Principal Investigator:
Abstract:
The typical critical current density of best Nb3Sn superconducting composite is approximately 1600 A/mm2 at 15T and 4.2K. This density is achieved in RRP® strand with ternary alloy of either (Nb,Ti)3Sn or (Nb,Ta)3Sn. This objective of this study is to improve superconducting property of (Nb, Ta,… More

Reduction of Porosity for High Critical Current Density Bi-2212 Superconductor Wire

Award Year / Program / Phase:
2010 / SBIR / Phase I
Award Amount:
$99,030.00
Agency:
DOE
Principal Investigator:
Abstract:
The Department of Energy is seeking superconducting material for a very high-field magnet to be used in a future particle accelerator. Bi-2212 round wire, a high temperature superconductor, is one of the best candidates for this purpose. However, there are significant amount of pores present in the… More

Improving High Field Critical Current Density of Nb3Sn Superconductor

Award Year / Program / Phase:
2011 / SBIR / Phase I
Award Amount:
$111,363.00
Agency:
DOE
Principal Investigator:
Seungok Hong, Dr. – 908 313 8514
Abstract:
The typical critical current density of best Nb3Sn superconducting composite is approximately 1600 A/mm2 at 15T and 4.2K. This density is achieved in RRP strand with ternary alloy of either (Nb, Ti)3Sn or (Nb,Ta)3Sn. This objective of this study is to improve superconducting property of… More

On The Use of Highly Densified Bi-2212 Wire for Superconducting Magnet Application

Award Year / Program / Phase:
2012 / SBIR / Phase I
Award Amount:
$145,022.00
Agency:
DOE
Principal Investigator:
Seungok Hong, Dr. – 908 313 8514
Abstract:
The Department of Energy is seeking ancillary technologies to enhance the performance of high filed superconducting materials critical for the very high-field magnets to be used in a future particle accelerator. Bi-2212 round wire, a high temperature superconductor, is one of the best candidates for… More