Novel Joining Technique for Oxide-Dispersion Strengthened Iron Aluminide Alloys

Award Information
Agency:
Department of Energy
Branch
n/a
Amount:
$0.00
Award Year:
2001
Program:
SBIR
Phase:
Phase I
Contract:
DE-FG03-00ER83041
Award Id:
54964
Agency Tracking Number:
60754S00-II
Solicitation Year:
n/a
Solicitation Topic Code:
n/a
Solicitation Number:
n/a
Small Business Information
7960 South Kolb Road, Tucson, AZ, 85706
Hubzone Owned:
N
Minority Owned:
N
Woman Owned:
N
Duns:
n/a
Principal Investigator:
Jared Sommer
Senior Research Scientist
(520) 574-1980
mercorp@mercorp.com
Business Contact:
James Withers
Chief Executive Officer
(520) 574-1980
jcwithers@mercorp.com
Research Institute:
n/a
Abstract
60754 Oxide-dispersion strengthened (ODS) iron aluminide alloys have been shown to exhibit high creep strength and excellent corrosion resistance. However, it is difficult to join the alloys because the dispersed oxides agglomerate, thus compromising the mechanical properties of the base material. Diffusion bonding, in which two clean surfaces are joined by diffusion under high temperature and pressure, would be a candidate solution, but residual surface oxide contamination can cause lower fracture toughness and ductility of the joint. This project will utilize a pulsed electric field during diffusion bonding to join ODS intermetallic materials at lower pressures and shorter times. In this processing technique, no alloying elements are used in the joined interface, leading to joint strengths near those of the base material at high temperature. In Phase I, MA956 rods that were diffusion-bonded for only 30 minutes at low pressure, using pulsed-electric field conditions, showed substantially higher strength than specimens fabricated without the pulsed electric field. Ultrasonic and x-ray analysis suggested that the pulsed electric field enhanced metal diffusion across the interface. In Phase II, the pulse-bonding technology will be statistically tested using a wider range of experimental conditions, including pressure, variation of temperature, and pulsing conditions. High-temperature tensile testing will be conducted on MA956 and Fe3Al rods and tubes. Sequential creep testing and environmental characterization under oxidizing and sulfidizing atmospheres will also be performed. Commercial Applications and Other Benefits as described by the awardee: The major application of this technology will be in the manufacture of iron aluminide components for high-temperature turbines and coal gasification furnaces. The pulse-bonding technology may be applicable for bonding other types of dissimilar metals and ceramics for automotive and aerospace applications

* information listed above is at the time of submission.

Agency Micro-sites


SBA logo

Department of Agriculture logo

Department of Commerce logo

Department of Defense logo

Department of Education logo

Department of Energy logo

Department of Health and Human Services logo

Department of Homeland Security logo

Department of Transportation logo

Enviromental Protection Agency logo

National Aeronautics and Space Administration logo

National Science Foundation logo
US Flag An Official Website of the United States Government